(3) rake face roughness when grinding smaller chips to avoid sticking knife phenomenon, before the tool, carefully sharpened flank to ensure a smaller roughness value, thereby reducing the chip flow resistance, stainless steel Furniture stores, avoid chips sticking knife. (4) should be kept sharp tool edge tool edge should be kept sharp to minimize work hardening, feed rate and cutting tool back should not be too small, the city population stainless steel furniture, in order to prevent the cutting tool in the hardened layer, the impact tool use life. Stainless steel rusty reason electrochemical corrosion pollution: exposure caused by scratches and corrosion medium and carbon steel form the original cells to generate electrochemical corrosion. Cutting: cutting slag, spatter, etc. to produce electrochemical corrosion rust and corrosion medium adhesion material form the original battery. Grilled school: ingredients change and uneven flame heating zone occurs and microstructure, high-grade stainless steel furniture, and produce electrochemical corrosion and corrosive media, the formation of a galvanic cell. Welding: welding area of ??physical defects (undercut, pores, cracks, lack of fusion, incomplete penetration, etc.) and chemical defects (coarse grains, the grain boundary chromium depletion, segregation, etc.) and corrosive media, the formation of primary batteries produce electrochemical corrosion . Material: stainless steel chemical defects (unevenness ingredients, S, P impurities, etc.) and physical surface defects (loose, sand holes, cracks, etc.) in favor of the formation of corrosive media and primary batteries produce electrochemical corrosion. Passivation: stainless steel pickling passivation effect caused by bad or uneven surface passivation film is thin, easy to form an electrochemical corrosion. Cleaning: product and stainless steel parts remaining residue with a stainless steel pickling passivation chemical corrosion formation of electrochemical corrosion. Stress concentration is liable to cause stress corrosion cracking (3) when the rake face grinding roughness smaller chips to avoid the phenomenon of sticking knife, before the tool, the flank grinding carefully to ensure a smaller roughness value, thereby reduce the chip flow resistance, custom stainless steel furniture, avoid chips sticking knife. (4) should be kept sharp tool edge tool edge should be kept sharp to minimize work hardening, feed rate and cutting tool back should not be too small, in order to prevent the cutting tool in the hardened layer, affecting the tool life. CHENGKOU Arts Yiu stainless steel furniture _ _ family steel furniture is provided by Chongqing Yao Yi Stainless Steel Products Co. CHENGKOU Arts Yiu stainless steel furniture _ _ family steel furniture is Chongqing Yao Yi Stainless Steel Products Co. (www.shudumy.com) this year introduced a new upgrade, the above picture is for reference only, please call the contact picture on this page or telephone obtain the latest information, contact: Mr. Chen.