Stainless steel rusty reason electrochemical corrosion pollution: exposure caused by scratches and corrosion medium and carbon steel form the original cells to generate electrochemical corrosion. Cutting: cutting slag, spatter, etc. to produce electrochemical corrosion rust and corrosion medium adhesion material form the original battery. Grilled school: Ingredients flame heating zone to produce electrochemical corrosion and microstructure changes and uneven, and corrosive media, the formation of a galvanic cell. Welding: welding area of ??physical defects (undercut, pores, cracks, lack of fusion, incomplete penetration, etc.) and chemical defects (coarse grains, the grain boundary chromium depletion, segregation, etc.) and corrosive media, the formation of primary batteries produce electrochemical corrosion . Material: stainless steel chemical defects (unevenness ingredients, S, P impurities, etc.) and physical surface defects (loose, sand holes, cracks, etc.) in favor of the formation of corrosive media and primary batteries produce electrochemical corrosion. Passivation: stainless steel pickling passivation effect caused by poor surface passivation film uneven or thin, stainless steel furniture store, easy to form an electrochemical corrosion. Cleaning: product and stainless steel parts remaining residue with a stainless steel pickling passivation chemical corrosion formation of electrochemical corrosion. Cause advantage liable to cause stress concentration is not easy oxidation stress corrosion of stainless steel, high-grade stainless steel furniture, the corrosion resistance of stainless steel of various different types, easy to shape, to do all kinds of crafts, Jiangjin stainless steel furniture, stainless steel rusty metallic strong electrochemical Corrosion of carbon steel contamination: Exposure caused by scratches and corrosion medium and carbon steel form the original cells to generate electrochemical corrosion. Cutting: cutting slag, spatter, etc. to produce electrochemical corrosion rust and corrosion medium adhesion material form the original battery. Grilled school: Ingredients flame heating zone to produce electrochemical corrosion and microstructure changes and uneven, and corrosive media, the formation of a galvanic cell. Welding: welding area of ??physical defects (undercut, pores, cracks, lack of fusion, incomplete penetration, etc.) and chemical defects (coarse grains, the grain boundary chromium depletion, segregation, etc.) and corrosive media, the formation of primary batteries produce electrochemical corrosion . Material: stainless steel chemical defects (unevenness ingredients, S, P impurities, etc.) and physical surface defects (loose, sand holes, cracks, etc.) in favor of the formation of corrosive media and primary batteries produce electrochemical corrosion. Passivation: stainless steel pickling passivation effect caused by bad or uneven surface passivation film is thin, easy to form an electrochemical corrosion. Cleaning: product and stainless steel parts remaining residue with a stainless steel pickling passivation chemical corrosion formation of electrochemical corrosion. Stress concentration is liable to cause stress corrosion of stainless steel furniture CASE, Yi Yiu stainless steel furniture is provided by family Yao Yi Stainless Steel Products Co. Chongqing. Jiangjin stainless steel furniture, art Yiu stainless steel, stainless steel furniture, household Chongqing Yao Yi Stainless Steel Products Co., Ltd. (www.shudumy.com) this year introduced a new upgrade, the above picture is for reference only, please call the telephone or pictures on this page, For the latest information, contact: Mr. Chen.