Acid-resistant stainless steel cutting and beveling usually directly through the cutting oxygen jet with iron, iron by means of heat in the ordinary oxygen-acetylene flame produced. Fused iron oxide and chromium oxide are mixed, and they are diluted to a significant amount of heat is increased, the formation of a mixture of liquid melt Li, is cut from the cut seam oxygen blowing. It can cut thick stainless steel sheet or cast appetite. Abroad, also use spray powder cutting method, with a fast fan cutting cutting nozzle, cutting nozzle at the outer edge of the flow of water spray, as shown in Figure 5 Wing. Iron particles generally greater than 150 mesh. V4 precision cut end up over stainless steel moldings, machining stainless verticality also ideal incision is not required for processing can achieve the requirements of the drawings. The flow of water jet cut heart pieces weeks, steel will not play at the end of Alice ridicule 5 jet cutting schematic ridicule cutting can improve the corrosion resistance of stainless steel cuts. Can be cut to 150 mm thick stainless steel pull wood, you can cut multiple layers 2--3 mm × 30 layers of ordinary carbon steel plate or 2 mm × 40 layers of stainless steel. If fitted profiling mechanism, but also cut into various shapes of patterns. It can be cut out, you can also manually operate it with plasma cutting shed ratio: simple equipment, light weight, easy does not require a large power supply, operation, stainless steel tip with a sprinkler door, reduce dust pollution. But it's no cutting speed plasma arc cutting was restored, and it can not cut copper embossed stainless steel plates, aluminum and its alloys. Chongqing stainless steel processing of stainless steel hardening heat treatment and quenching and tempering main purpose is hardening, after the hardening material is heated to a temperature below the phase transition point, the use of appropriate hardening prick rapid cooling. In order to improve the toughness after tempering is quenched material, to obtain the desired degree of heat treatment is carried out. It is heated to a temperature as shown in the following transformation point Xu is cooled. It is believed that the heating rate and holding time is basically the same annealing conditions. For ferritic stainless steel type, heat treatment is intended to soften the tissue and adjusting end product organization, often annealing. Standard incubation time is based on the material thickness or diameter for every 25 mm, to be incubated for 1 hour or more terms, from the perspective of preventing deformation, should avoid excessive heating rate. Embossed stainless steel plates, stainless steel, Chongqing Yao Yi Stainless Steel Products Co. provided by Chongqing Yao Yi Stainless Steel Products Co., Ltd. Stainless Steel Products Co., Ltd. Chongqing Yi Yao (www.shudumy.com) strong, credible, in Chongqing, Chongqing stainless steel products and other industries and has accumulated a large number of loyal customers. The company better work attitude and constantly improving innovative ideas will lead the Arts Yiu stainless steel and you hand into the brilliant, for a better future!